Code FC-ZR-WH
Fusion White (ST / HT)
White zirconia for colouring with liquids: ST with high translucency and HT with high opacity for masking.
Price Price on request
Send an inquiry about this product
Description
Fusion white blanks are coloured with liquids, which gives unlimited shading possibilities.
- ST — high light transmission for shaded and unshaded restorations
- HT — a more opaque structure that covers unwanted reflections from within
- The White ST–HT group reaches a strength of 1300 MPa and above
- Compatible with incisal-occlusal effect kits applied before sintering
The HT group is also suitable when the patient wants a completely white look.
Technical details
- Indications
- Substructures, bridges of up to 16 units
- Pressing
- Isostatic (CIP)
- Strength
- 1250 MPa in the dentin area
- Light transmittance
- 48 %
- Shading
- White, for colouring with liquids
- Types
- White (ST), HT
- Minimum thickness
- 0.6 mm
- Glazing temperature
- 740–980 °C
- Glazing, 1–3 units
- B 400 °C, S 6 min, t 45 °C/min, T 900 °C, H 1 min, vacuum 0/0, L 750 °C
- Glazing, 4 units and more
- B 400 °C, S 6 min, t 35 °C/min, T 900 °C, H 1 min, vacuum 0/0, L 550 °C
- Heights
- 10, 12, 14, 16, 18, 20, 22, 25, 30 mm
- Sintering programme
- 20 → 300 °C at 10 °C/min; 10 min hold; 300 → 1500 °C at 5 °C/min; 2 h hold at 1500 °C; cooling at 5 °C/min to 200 °C, then natural cooling