Code FC-ZR-ML7
Fusion Multilayer
Seven-layer blank with a smooth shade gradient and 1250 MPa strength — for full restorations and bridges of up to 16 units.
Description
Multilayer has 7 shade layers instead of the usual 3–4, so the transition from the cervical area to the incisal edge is smooth and natural. Its strength of 1250 MPa (class 5) places it among the strongest multilayer blanks on the market.
It is produced in all Vita classic shades and in bleach shades. For customers who find White too white and OM1 too dark, the manufacturer developed the intermediate shade OM0.5.
Aesthetic tip: with the cutback or make-up technique, apply the stains to the cervical and equatorial areas. The incisal-occlusal area contains less pigment and may look whiter — cover it with build-up or make-up.
Technical details
- Indications
- Full restorations, bridges of up to 16 units
- Pressing
- Isostatic (CIP)
- Strength
- 1250 MPa in the dentin area
- Light transmittance
- 52 %
- Layers
- Transition across 7 dentin layers and a translucent layer
- Minimum thickness
- 0.6 mm
- Glazing temperature
- 740–980 °C
- Glazing, 1–3 units
- B 400 °C, S 6 min, t 45 °C/min, T 900 °C, H 1 min, vacuum 0/0, L 750 °C
- Glazing, 4 units and more
- B 400 °C, S 6 min, t 35 °C/min, T 900 °C, H 1 min, vacuum 0/0, L 550 °C
- Heights
- 14, 16, 18, 20, 22, 25 mm
- Shades
- A1, A2, A3, A3.5, A4, B1, B2, B3, B4, C1, C2, C3, C4, D2, D3, D4 and bleach OM0.5, OM1, OM2, OM3
- Sintering programme
- 20 → 300 °C at 10 °C/min; 10 min hold; 300 → 1500 °C at 5 °C/min; 2 h hold at 1500 °C; cooling at 5 °C/min to 200 °C, then natural cooling