Code FC-LS2-P
Fusion Press LS2
Lithium disilicate pressing ingots with a strength of 550 MPa, in HT and MT series.
Price Price on request
Send an inquiry about this product
Description
Fusion Press LS2 has a strength of 550 MPa thanks to its strong structure.
- HT (high translucency) — a glassy look at thicknesses below 1 mm
- MT (medium translucency) — for all restorations with cutback or substructures
- MT in bleach shades — blocks reflections from the stump, suitable for a Hollywood smile
- Can be finished without porcelain thanks to its light transmission
- After mechanical smoothing with rubber polishers it can be glazed with Mono Glaze at low temperature
Tips: do not sandblast perpendicular to the surface, at more than 2 bar or with sand coarser than 50 µm. Do not overheat when cutting connectors and do not cool suddenly in water. During firing, support the restoration on a porcelain pillow; the thinnest areas must be at least 0.5 mm.
Technical details
- Material
- Lithium disilicate for pressing
- Strength
- 550 MPa
- Series
- HT (high translucency), MT (medium translucency)
- Shades
- BL1, A1, A2, A3, B1
- Pressing MT, 100 g investment
- B 700 °C, t 60 °C/min, T 915 °C, H 15 min, L 250 °C
- Pressing HT, 100 g investment
- B 700 °C, t 60 °C/min, T 910 °C, H 15 min, L 250 °C
- Pressing MT, 200 g investment
- B 700 °C, t 60 °C/min, T 915 °C, H 25 min, L 250 °C
- Pressing HT, 200 g investment
- B 700 °C, t 60 °C/min, T 910 °C, H 25 min, L 250 °C